Ron Roy on wed 29 jul 09
Hi Jean,
I'm assuming cone 10 - cause it won't melt at cone 6.
You will not see any difference using the old G200 or the new version.
RR
On Sun, Jul 26, 2009 at 8:59 PM, Jean W. Cochran wro=
te:
> Dear Fellow Clayarters,
>
> I plan to make up this glaze very soon. I will be firing it oxidation, i=
n
> an old electric kiln. My question is this: Can I directly substitute G2=
00
> for the Custer Feldspar? If not, what should my amounts be changed to?
>
> Thank you kindly,
>
>
> WARM BUTTER YELLOW
> Got from Rosey, she got from
> internet
>
> Dolomite 17.15
> EPK 19.76
> Bone Ash 5.93
> Custer Feldspar 40.83
> Silica 16.33
> Sub-Total 100
> Rutile 7.5
> Tin Oxide 0.5
>
>
>
> Jean Wadsworth Cochran
> www.foxhollowpottery.com
>
--
Ron Roy
15084 Little Lake Road
Brighton, Ontario, Canada
K0K 1H0
| |
|