Karen Sullivan on tue 7 nov 00
Ilene - The following is for cone 10
custer spar 31.7 %
silica 25.7
whiting 22.7
talc 7.7
epkaolin 12.3
copper carb 4.1
originally an oribe with less copper...
bamboo karen
John Hesselberth on wed 8 nov 00
Ilene,
This glaze will have marginal stability at best. Shaner's Oribe, which
is this glaze with a little more copper, is VERY unstable per testing
done by Tom Wirt and Betsy Price. I would not personally use this on
dinnerware without very careful testing.
Regards, John
ILENE MAHLER wrote:
>.Is
>this glaze safe for dinnerware..Is it soft will aknife cut it with thar
>much copper Thanks Ilene
>
>Karen Sullivan wrote:
>>
>> Ilene - The following is for cone 10
>>
>> custer spar 31.7 %
>> silica 25.7
>> whiting 22.7
>> talc 7.7
>> epkaolin 12.3
>> copper carb 4.1
>>
>> originally an oribe with less copper...
>>
>> bamboo karen
John Hesselberth
Frog Pond Pottery
P.O. Box 88
Pocopson, PA 19366 USA
EMail: john@frogpondpottery.com web site: http://www.frogpondpottery.com
"It is, perhaps, still necessary to say that the very best glazes cannot
conceal badly shaped pots..." David Green, Pottery Glazes
ILENE MAHLER on wed 8 nov 00
I will send the shino after xmas as the studio has all stuff away..Is
this glaze safe for dinnerware..Is it soft will aknife cut it with thar
much copper Thanks Ilene
Karen Sullivan wrote:
>
> Ilene - The following is for cone 10
>
> custer spar 31.7 %
> silica 25.7
> whiting 22.7
> talc 7.7
> epkaolin 12.3
> copper carb 4.1
>
> originally an oribe with less copper...
>
> bamboo karen
>
> ______________________________________________________________________________
> Send postings to clayart@lsv.ceramics.org
>
> You may look at the archives for the list or change your subscription
> settings from http://www.ceramics.org/clayart/
>
> Moderator of the list is Mel Jacobson who may be reached at melpots@pclink.com.
Karen Sullivan on wed 8 nov 00
I have no idea whether the glaze is food safe....
I guess you will need to test it.
karen
on 11/8/00 8:00 AM, ILENE MAHLER at imahler@HOME.COM wrote:
> I will send the shino after xmas as the studio has all stuff away..Is
> this glaze safe for dinnerware..Is it soft will aknife cut it with thar
> much copper Thanks Ilene
>
> Karen Sullivan wrote:
>>
>> Ilene - The following is for cone 10
>>
>> custer spar 31.7 %
>> silica 25.7
>> whiting 22.7
>> talc 7.7
>> epkaolin 12.3
>> copper carb 4.1
>>
>> originally an oribe with less copper...
>>
>> bamboo karen
>>
>>
____________________________________________________________________________
_>> _
>> Send postings to clayart@lsv.ceramics.org
>>
>> You may look at the archives for the list or change your subscription
>> settings from http://www.ceramics.org/clayart/
>>
>> Moderator of the list is Mel Jacobson who may be reached at
>> melpots@pclink.com.
>
> ______________________________________________________________________________
> Send postings to clayart@lsv.ceramics.org
>
> You may look at the archives for the list or change your subscription
> settings from http://www.ceramics.org/clayart/
>
> Moderator of the list is Mel Jacobson who may be reached at
> melpots@pclink.com.
>
| |
|