jeremy Kaiser on tue 2 dec 03
Does anyone know how to calcine Zinc Oxide for cone 10 crystal glazes. Any advice would be very helpful. JK
---------------------------------
Do you Yahoo!?
Free Pop-Up Blocker - Get it now
Graeme Anderson on tue 2 dec 03
I just put some zinc in an unglazed bowl during a bisc firing. - to about
790 C/1450 F
Cheers. Graeme.
On Tue, 2 Dec 2003 06:19:32 -0800, jeremy Kaiser
wrote:
>Does anyone know how to calcine Zinc Oxide for cone 10 crystal glazes. Any
advice would be very helpful. JK
>
>
>
>---------------------------------
>Do you Yahoo!?
>Free Pop-Up Blocker - Get it now
>
>___________________________________________________________________________
___
>Send postings to clayart@lsv.ceramics.org
>
>You may look at the archives for the list or change your subscription
>settings from http://www.ceramics.org/clayart/
>
>Moderator of the list is Mel Jacobson who may be reached at
melpots@pclink.com.
Ilene Mahler on wed 3 dec 03
calcine in a bisqued pot to 1000 degress you do not need to go higher as it
lumps..Ilene who has been there plenty
----- Original Message -----
From: "jeremy Kaiser"
To:
Sent: Tuesday, December 02, 2003 9:19 AM
Subject: Calcining Zinc Oxide
> Does anyone know how to calcine Zinc Oxide for cone 10 crystal glazes. Any
advice would be very helpful. JK
>
>
>
> ---------------------------------
> Do you Yahoo!?
> Free Pop-Up Blocker - Get it now
>
>
____________________________________________________________________________
__
> Send postings to clayart@lsv.ceramics.org
>
> You may look at the archives for the list or change your subscription
> settings from http://www.ceramics.org/clayart/
>
> Moderator of the list is Mel Jacobson who may be reached at
melpots@pclink.com.
| |
|