Gale Bez on sat 9 nov 02
Hi...... I'm a glass artist trying to formulate a low fire earthenware clay body that can be slabbed or thrown up to 1/2 inch thick and will not warp.
This clay needs to be coefficient compatible with coe 90 glass. Top end of firing range will not exceed 1400 degrees F. Cone 014 - 015.
Thanks for your help, Gale
lela martens on sun 10 nov 02
Hi Gale,
check out www.warmglass.com. It may have what you are looking for. Lela
Martens on the Canadian plains where the roads are frozen but at least it
isn`t blizzarding.(yet) And you guys are concernened about flies. We only
have a couple left in the house now, the weather takes care of them quick
enough. There are a few possitives living with Canadian winter. Best wishes
from Lela Martens in southern Alberta
>From: Gale Bez
>Reply-To: Ceramic Arts Discussion List
>To: CLAYART@LSV.CERAMICS.ORG
>Subject: Looking for low-low fire (cone 014?) clay body recipe
>Date: Sat, 9 Nov 2002 17:32:56 -0800
>
>Hi...... I'm a glass artist trying to formulate a low fire earthenware clay
>body that can be slabbed or thrown up to 1/2 inch thick and will not warp.
>
>This clay needs to be coefficient compatible with coe 90 glass. Top end of
>firing range will not exceed 1400 degrees F. Cone 014 - 015.
>
>Thanks for your help, Gale
>
>______________________________________________________________________________
>Send postings to clayart@lsv.ceramics.org
>
>You may look at the archives for the list or change your subscription
>settings from http://www.ceramics.org/clayart/
>
>Moderator of the list is Mel Jacobson who may be reached at
>melpots@pclink.com.
_________________________________________________________________
MSN 8 with e-mail virus protection service: 2 months FREE*
http://join.msn.com/?page=features/virus
| |
|